GATE MT 2013 Q19. For a good quality brazing, the molten filler alloy should have
GATE MT 2013 Q19. For a good quality brazing, the molten filler alloy should have
Share
Lost your password? Please enter your email address. You will receive a link and will create a new password via email.
Please briefly explain why you feel this question should be reported.
Please briefly explain why you feel this answer should be reported.
Please briefly explain why you feel this user should be reported.
Correct answer is option A. The molten filler alloy should have low contact angle with the base metal. As lowering the contact angle will increase the wettability.
Correct answer is option A.
The molten filler alloy should have low contact angle with the base metal. As lowering the contact angle will increase the wettability.