GATE MT 2017 17. Four alloys C1,C2, C3,C4 shown in the phase diagram are poured at a temperature T1 in a mould. During solidification, which one of these alloys is expected to have the highest fluidity?
Share
Lost your password? Please enter your email address. You will receive a link and will create a new password via email.
Please briefly explain why you feel this question should be reported.
Please briefly explain why you feel this answer should be reported.
Please briefly explain why you feel this user should be reported.
Option C is correct. Because at C3 there is a eutectic point at which melting point is low and has high fluidity. The other compositions have a freezing range where there are two different phases so fluidity decreases.
Option C is correct.
Because at C3 there is a eutectic point at which melting point is low and has high fluidity. The other compositions have a freezing range where there are two different phases so fluidity decreases.
See lessCorrect answer is option C. @Shetty described it best. Thank you.
Correct answer is option C. Sanjay Madishetty described it best. Thank you.
See less