A 250mm thick slab of nickel alloy is subjected to cold rolling using a roll of diameter 450mm. If the angle of bite during rolling is 10°, the maximum possible reduction (in mm) during rolling is ____ (answer up to two decimal places)
Share
Lost your password? Please enter your email address. You will receive a link and will create a new password via email.
Please briefly explain why you feel this question should be reported.
Please briefly explain why you feel this answer should be reported.
Please briefly explain why you feel this user should be reported.
Correct answer is 6.97 we know that, μ=tan Θ given Θ= 100 Maximum possible reduction= Δh=μ2R= (tan 10)2×225= 6.97 mm
Correct answer is 6.97
we know that, μ=tan Θ
given Θ= 100
Maximum possible reduction= Δh=μ2R= (tan 10)2×225= 6.97 mm