The c/a ratio of Zn (hcp) is 1.856. Slip at room temperature occurs most easily on which of the following slip systems in Zn:
Note: In hcp metals, the ideal c/a ratio is 1.633.
(A) {11̅00} 〈112̅0〉 (B) {11̅00} 〈0002〉
(C) {0001} 〈112̅0〉 (D) {101̅1̅} 〈112̅3〉
Get every updates in your mailbox!
The c/a ratio is greater than the ideal ratio of 1.633 hence, the slip should occur on the basal plane that is {0001} Option C
The c/a ratio is greater than the ideal ratio of 1.633 hence, the slip should occur on the basal plane that is {0001}
Option C
See lessCorrect answer is option C. @digbijaya igit described it best. Thank you.
Correct answer is option C. digbijaya igit igit described it best. Thank you.
See lessCan You Elaborate It More. Because, I'm Not Getting It.Explain In Another Way.Plzzz.......🙏🙏🙏🙏🙌
Can You Elaborate It More. Because, I’m Not Getting It.
See lessExplain In Another Way.
Plzzz…….🙏🙏🙏🙏🙌
Option C because slip occur at basal plane in hcp
Option C because slip occur at basal plane in hcp