GATE MT 2018 Q14.Which of the following welding processes is NOT suitable for joining thin metal sheets?
GATE MT 2018 Q14.Which of the following welding processes is NOT suitable for joining thin metal sheets?
Share
Lost your password? Please enter your email address. You will receive a link and will create a new password via email.
Please briefly explain why you feel this question should be reported.
Please briefly explain why you feel this answer should be reported.
Please briefly explain why you feel this user should be reported.
Get every updates in your mailbox!
Electroslag welding is used mainly to join low carbon steel plates and/or sections that are very thick.
Electroslag welding is used mainly to join low carbon steel plates and/or sections that are very thick.
See lessB
B
See lessCorrect answer is option B. @Arpita Samal described it best. Thank you.
Correct answer is option B. Arpita Samal described it best. Thank you.
See lessDeposition rate is very high in electro slag welding and that too very difficult to hold the push with thin plates It is usually used for high deposition rate joints and also economical...
Deposition rate is very high in electro slag welding and that too very difficult to hold the push with thin plates
See lessIt is usually used for high deposition rate joints and also economical…
Electroslag welding as it used for welding thick plates.
Electroslag welding as it used for welding thick plates.