If 2 moles of Au and 3 moles of Ag are mixed to form a single-phase ideal solid solution, the total entropy of mixing is _____(on J K–1 to one decimal place )
Given: Gas constant R = 8.314 J K-1 mol-1
Lost your password? Please enter your email address. You will receive a link and will create a new password via email.
Please briefly explain why you feel this question should be reported.
Please briefly explain why you feel this answer should be reported.
Please briefly explain why you feel this user should be reported.

See lessCorrect answer is 27.97 @Digbijaya igit described it best. Thank you.
Correct answer is 27.97 digbijaya igit igit described it best. Thank you.
See lesswe can calculate by S=-RT(Xa.lnXa + Xb.lnXb)
we can calculate by
S=-RT(Xa.lnXa + Xb.lnXb)
See lessT will not be there in ΔSmix