GATE MT 2019 Q28
The length of internal cracks in the two samples of same glass is measured to be C1= 0.5mm and C2= 2mm. The ratio of (σ1/σ2) of the fracture strength of the two samples is ______.
Share
Lost your password? Please enter your email address. You will receive a link and will create a new password via email.
Please briefly explain why you feel this question should be reported.
Please briefly explain why you feel this answer should be reported.
Please briefly explain why you feel this user should be reported.
Using Griffith's theory ratio of fracture strength if two samples is 2 (option C)
Using Griffith’s theory ratio of fracture strength if two samples is 2 (option C)
See less
See lessCorrect answer is option C. @Digbijaya igit described it best. Thank you. Some peripheral lines related to this topic: Griffith's theory: σ=√2Eγ/πc
Correct answer is option C. digbijaya igit igit described it best. Thank you.