GATE MT 2020 Q21. A slip system consists of a slip plane and a slip direction. Which one of the following is NOT a valid slip system in a FCC copper crystal?
Share
Lost your password? Please enter your email address. You will receive a link and will create a new password via email.
Please briefly explain why you feel this question should be reported.
Please briefly explain why you feel this answer should be reported.
Please briefly explain why you feel this user should be reported.
It can easily be found by simple plane and direction condition. Since the slip direction must lie in the slip plane so if (hkl)- slip plane and [uvw]- slip direction then by direction will lie in plane if hu+kv+lw=0 . So by que, B option is the only system which didn't satisfy this. That means it doRead more
It can easily be found by simple plane and direction condition.
Since the slip direction must lie in the slip plane so if (hkl)- slip plane and [uvw]- slip direction then by direction will lie in plane if hu+kv+lw=0 .
So by que,
B option is the only system which didn’t satisfy this. That means it doesn’t lie in slip plane and hance not a slip system.
See lessCorrect answer is option B. @Rohit.km described it best. Thank you. Some peripheral lines related to this topic: (hkl) [uvw] are said to be slip system hu + kv + lw = 0
Correct answer is option B. Rohit jha.km described it best. Thank you.
Some peripheral lines related to this topic:
hu + kv + lw = 0
B
B
See lessFor a valid slip system there is a condition given below; slip direction * slip plane = 0 so 1*0+1*1+1**1 = 2 which is not equal to zero hence B is correct
For a valid slip system there is a condition given below;
slip direction * slip plane = 0
so 1*0+1*1+1**1 = 2 which is not equal to zero
See lesshence B is correct