From high temperature tensile testing, the flow stress (measured at the same value of strain) of an alloy was found to be 50 MPa at a strain rate of 0.1 s–1 and 70 MPa at a strain rate of 10 s–1. The strain rate sensitivity parameter is (round off to 3 decimal places).