In Thomas process P, Mn, C removes but not Silicon. why?
Share
Connect with:
or use
Have an account? Sign In Now
Lost your password? Please enter your email address. You will receive a link and will create a new password via email.
Please briefly explain why you feel this question should be reported.
Please briefly explain why you feel this answer should be reported.
Please briefly explain why you feel this user should be reported.
One difficulty with Bessemer's process/ Thomas process was that it could convert only a pig iron low in phosphorus and sulfur. (These elements could have been removed by adding a basic flux such as lime, but the basic slag produced would have degraded the acidic refractory lining of Bessemer's conveRead more
One difficulty with Bessemer’s process/ Thomas process was that it could convert only a pig iron low in phosphorus and sulfur. (These elements could have been removed by adding a basic flux such as lime, but the basic slag produced would have degraded the acidic refractory lining of Bessemer’s converter).