What is hardening temperature?
Share
Lost your password? Please enter your email address. You will receive a link and will create a new password via email.
Please briefly explain why you feel this question should be reported.
Please briefly explain why you feel this answer should be reported.
Please briefly explain why you feel this user should be reported.
The hardening process consists of heating the components above the critical (normalizing) temperature, holding at this temperature for one hour per inch of thickness cooling at a rate fast enough to allow the material to transform to a much harder, stronger structure. Henceforth the temperature at wRead more
The hardening process consists of heating the components above the critical (normalizing) temperature, holding at this temperature for one hour per inch of thickness cooling at a rate fast enough to allow the material to transform to a much harder, stronger structure. Henceforth the temperature at which this process takes place is called the hardening temperature which varies according to the composition of components.
See lesstemperature of austenization from where quenching is done
temperature of austenization from where quenching is done
See lessIf metal have 800c by cooling it into water tank and also you can put into oil tank to quench it's . this process is called hardening
If metal have 800c by cooling it into water tank and also you can put into oil tank to quench it’s . this process is called hardening