Why Ferrosilicon is used in the pidgeon process?? In place of Fesi can we use Mn-Si ?
[email protected]Platinum
Why Ferrosilicon is used in the pidgeon process?? In place of Fesi can we use Mn-Si ?
Share
Lost your password? Please enter your email address. You will receive a link and will create a new password via email.
Please briefly explain why you feel this question should be reported.
Please briefly explain why you feel this answer should be reported.
Please briefly explain why you feel this user should be reported.
Ferrosilicon is used as pure Si cannot be used for reduction. MnSi can be used but there is no information how it shall behave.
Ferrosilicon is used as pure Si cannot be used for reduction.
MnSi can be used but there is no information how it shall behave.