Why precipitate nucleate inside the grain rather than grain boundary when ot quenched?
Share
Lost your password? Please enter your email address. You will receive a link and will create a new password via email.
Please briefly explain why you feel this question should be reported.
Please briefly explain why you feel this answer should be reported.
Please briefly explain why you feel this user should be reported.
Get every updates in your mailbox!
Hey Suraj, By allowing precipitation to occur at much below the solvous line, precipitation at grain boundaries can be avoided. At this temperature nucleation at grain boundary is not easy because at this temperature atoms cannot move to the grain boundary (diffusion rates are not high). So, the preRead more
Hey Suraj,
By allowing precipitation to occur at much below the solvous line, precipitation at grain boundaries can be avoided. At this temperature nucleation at grain boundary is not easy because at this temperature atoms cannot move to the grain boundary (diffusion rates are not high). So, the precipitation will occur inside the grain.
See lessthank u....
thank u….
See less