why sinter is used upto 50%, but pellet 15-20% in blast furnace burden even though pellets have good permeability?
why sinter is used upto 50%, but pellet 15-20% in blast furnace burden even though pellets have good permeability?
Share
Lost your password? Please enter your email address. You will receive a link and will create a new password via email.
Please briefly explain why you feel this question should be reported.
Please briefly explain why you feel this answer should be reported.
Please briefly explain why you feel this user should be reported.
The cost of the pellets making process is very expensive compare to sinter making process. That's why we are using little pellets to improve burden quality.
The cost of the pellets making process is very expensive compare to sinter making process. That’s why we are using little pellets to improve burden quality.
See lessIts not a prefluxed raw material & simultaneously uses of higher percentage of Pellet is not economic. production cost will go higher side.
Its not a prefluxed raw material & simultaneously uses of higher percentage of Pellet is not economic.
production cost will go higher side.
See lessPellets formation is bit expensive and pellets are formed from low grade ores and doesn't have much strength as compared to sintered ores.
Pellets formation is bit expensive and pellets are formed from low grade ores and doesn’t have much strength as compared to sintered ores.
See less